Nimonic 105 is a Ni-Co-Cr-based precipitation hardening deformation superalloy, the service temperature is 750℃-950℃. Nimonic105/alloy has high room temperature and high temperature strength, good oxidation resistance, but general hot workability and welding performance. It is suitable for manufacturing high-temperature parts such as aero-engine turbine blades and high-temperature bolts. The main products are hot-rolled bars, flat bars, cold-drawn bars, profiles and ring parts.
Nimonic 105 has been used in the manufacture of aero-engine turbine blades, fan-shaped seals, high-temperature bolts and other parts, and the batch production and use are in good condition.Nimonic 105has high resistance to deformation and should be prevented from cracking during forging and rolling. The suitable cold drawing temperature for cold drawn bars is about 600°C.

  • نبذة عن المنتج:
  • استفسار

الموديل: Nimonic 105
الماركة: RONSCO



RONSCO  Alloy 105 Parameter Table
NIMONIC® alloy 105, UNS N13021, W.Nr.2.4634, MSRR 7017, MSRR 7018
مقدمة عامة
NIMONIC® alloy 105 (UNS N13021/W. Nr. 2.4634) is a forged Ni-Co-Cr base alloy and strengthened by additions of Mo,AI & Ti.It can work up to 950°C. Alloy 105 combines the high strength of the age-hardening nickel-base alloys with good creep resistance. For critical applicationsthe alloy is produced by vacuum melting and electroslag refining.The alloy is used for turbine blades, discs, forgings, ring sections, bolts and fasteners.
Alloy 105 has excellent heat resistant properties, high strength and oxidation resistance. The high creep-rupture properties of Alloy 105 makes the alloy perfect for critical gas turbine applications. Alloy 105 can be heat treated as followed; For optimum long term creep and ductility at 850-950°C:4 hours at 1150°C, 16 hours at 1050-1065 °C and 16 hours at 850°C with air cooling after all heat treatment operations. Where tensile strength, elongationand impact stength are more critical at temperature up to 700°C: 4 hours at 1125°C and 16 hours at 850°C with air cooling after all heat treatment operations.
التركيب الكيميائي:
وصف المنتجCSi MnSPCrCoMoNiFeBZrAITiPbCu
اقل شئ




14.00 18.00 4.50 BAL
0.003 
4.50 0.90 

اكثر شئ0.170 1.00 1.00 0.010.045 15.70 22.00 5.50 BAL1.00 0.01 0.15 4.90 1.50 0.00150.20 

النماذج والمواصفات
Standards: ASTM B637, MSRR 7004, 7022, 7063, 7070, 7162, 7193, 7952, BS: HR 203, 3HR1, HR2, HR3, HR4, BS4HR 601

This alloy has good ductility and may be readily formed by all conventional methods. Because the alloy is stronger than regular steel it requires more powerful equipment to accomplish forming. Heavy-duty lubricants should be used during cold forming. It is essential to thoroughly clean the part of all traces of lubricant after forming as embrittlement of the alloy may occur at high temperatures if lubricant is left on.
الخصائص الفيزيائية:تطبيق:
Density: 8.01 g/cm³, 0.289 lb/in³
Melting Range Liquidus temperature:  1345°C
Solidus temperature: 1290°C
Specific Heat Capacity: 419 J/kg.°C
Electrical Resistivity: 1.31 µΩ.m
Two heat treatments are as follows:
(a) 4 h/1150°C/AC+16 h/1050-1065°C/AC+16h/850°C/AC
(b) 4 h/1125°C/AC+16 h/850°/AC
ريش التوربينات
Turbine discs
Turbine shafts
المطروقات
Rolled rings
Bolts and fasteners

الخصائص الميكانيكية والفيزيائية
الخصائص الميكانيكية والفيزيائية21.1 درجة مئوية93.3 درجة مئوية148.9 درجة مئوية204.4 درجة مئوية315.6 درجة مئوية371.1 درجة مئوية426.7 درجة مئوية537.8 درجة مئوية648.9 درجة مئوية750 درجة مئوية815 درجة مئوية870 درجة مئوية982 درجة مئوية
Ultimate Tensile Strength /MPa114011231123108410911101110110641038---175
0.2% Yield Strength /MPa776762762735735743743740720---152
الحد من منطقة ٪313131383039393738---73
استطالة ٪222020212024242325---42
Minimum Creep 0.0001% per hr--------4282329354-
10,000 hr Rupture Strength--------4712631356512
Coefficient of Thermal Expansion /µm/m°C12.212.212.212.813.113.413.413.714---18
Thermal Conductivity /kcal/(hr.m.°C)9.36310.4110.4111.6712.8914.0414.0415.216.02---22.54
Modulus of Elasticity / GPa188184184179174168168161154---110

ميزة رونسكو
1,سعر أقل من أوروبا والولايات المتحدة الأمريكية 30٪.
2,ضمان الجودة بنسبة 100٪ لأننا نعيد صهرنا بواسطة VIM + VAR.
2,أفضل خدمة: 0 دفع إذا لم يكن الاختبار على ما يرام. 
3,0 رسوم UT ، PT. 
4,موك للمواد الجديدة: 600 كجم.
5,سريع 20 إلى 30 يومًا من المهلة الزمنية للمواد الجديدة.


For more information about Nimonic 105 (UNS N13021/W. Nr. 2.4634)  Pipes & Tubes, Sheet & Plates, Round Bars & Rods, Wire, Forgings Etc, please call +86 17708476248 أو إرسال بريد إلكتروني إلى [[البريد الإلكتروني محمي]]